Inconel 601 is a nickel-based high-temperature alloy whose main components are nickel, chromium, aluminum and iron. Nickel accounts for the majority, with a content generally above 58%, while chromium and aluminum account for about 19% and 1.0% respectively. In addition, it also contains small amounts of elements such as copper and manganese, which can enhance the strength and corrosion resistance of the material. Inconel 601 pipes are of excellent high temperature strength, corrosion resistance and oxidation resistance. At high temperatures, its strength and hardness can be maintained at a high level, while having good plasticity and toughness. In an acidic environment, Inconel 601 pipe performs good corrosion resistance and can effectively resist erosion by corrosive media such as chloride ions and sulfides.

Product Parameters

Product Name		Inconel 601 Pipe
Outer Diameter	Round Pipe	4mm-200mm
	Square Pipe	10*10mm-100*100mm
	Rectangular Pipe	10*20mm-50*100mm
Wall Thickness		0.6mm-6.0mm
Length		1-6 meters, Length can be customized
Standard		ASTM, AISI, JIS, GB, DIN, EN, etc.
Surface		Black, Bright Polished, Rough Turning, Matt Surface Treatment, No.4, BA, etc.
Certificate		ISO, SGS, BV
Production Technology		Hot Rolling, Cold Rolling

Chemical Composition

C	Al	Si	S	Cr	Mn	Fe	Ni	Cu
0.1 max	1.0-1.7	0.5 max	0.015 max	21.0-25.0	1.0 max	Remainder	58.0-63.0	1.0 max

Mechanical Properties

Tensile Strength (ksi)	0.2% Yield Strength (ksi)	Elongation% in 2 inches
80	30	30

Physical Performance

	Units	Temperature in°C
Density	8.11 g/cm³	Room
Specific Heat	0.107 Kcal/kg.C	20°
Melting Range	1360-1411°C	–
Modulus of Elasticity	206.5 KN/mm²	20°
Electrical Resistivity	118 µΩ.cm	20°
Coefficient of Expansion	13.75 µm/m °C	20 – 100°
Thermal Conductivity	11.2 w/m-° K	20°

Scope of Application

The 601 characteristics of Inconel make it widely used in the fields of heat treatment, chemical treatment, pollution control, aerospace and power generation. Therefore, it is not recommended to use the alloy 601 in a strongly reduced sulfur-containing environment.lution control equipment and nuclear reactors.pment, nuclear fuel reprocessing and pickling equipment.